Healing ceramic electrolyte degraded by lithium dendrite – Tech Xplore
A research team in the Department of Electrical and Electronic Information Engineering at Toyohashi University of Technology and the Department of Chemistry at…
A research team in the Department of Electrical and Electronic Information Engineering at Toyohashi University of Technology and the Department of Chemistry at University of Calgary has investigated the effect of post-annealing for healing Li garnet solid electrolyte degraded by the growth of Li dendrites. The ionic conductivity of the annealed solid electrolyte was slightly lower than that of the electrolyte before annealing but was retained above 10-4 S cm-1 at room temperature. The electrochemical…
-
Noosa News20 hours agoTerrifying break-in at childcare centre on Sunshine Coast ends with death of man
-
General22 hours agoTrial of celebrity crocodile wrangler Matt Wright to hear from more witnesses
-
Noosa News21 hours agoWhy the Story Bridge won’t have a traffic lane repurposed for bikes and walkers
-
General23 hours agoPM kicks off roundtable with call for lasting reform